Unsaturated polyester resins for layering, molding, with general application General Purpose
The resins of this group are designed for use in the production of composite parts manually. These resins can also be used in making all kinds of sculptures, hard and soft molds, producing fiberglass sheets with reasonable prices, high mechanical properties and easy application.
Orthophthalic polyester resin for making all kinds of general purpose composite parts | Paya pol 500 Paya pol 575 Paya pol 590 Paya pol 545 Paya pol 525 Paya pol 800 |
Orthophthalic polyester resin with excellent mechanical properties for composite and molding | Paya pol 410 Paya pol 420 |
Orthophthalic polyester resin for making all kinds of fiberglass sheets | Paya pol 565 Paya pol 590 |
Orthophthalic polyester resin for sculpture and molding | Paya pol 525 Paya pol 520 Paya pol 575 Paya pol 800 |
Orthophthalic polyester resin for chemical resistance and molding | Paya pol 430 |
Chemical nature – Based on orthophthalic acid and standard glycols Advantages – Medium reactivity – Good lamination and wetting ability – Good mechanical properties including strain in failure and optimal HDI Applications – Pipe construction – Vessel – Technical data connections
Appearance properties | |||
Color | Gardner | <2 |
Physical properties | |||
Solid Content | % | 64 ± 2 | |
Density | g / ml | 1.12 – 1.15 | |
Viscosity | cP | 400 ± 25 | 25 ° C |
Shrinkage | % | Approximately 2.2 | Internal Method, Linear Shrinkage |
Thermal properties | |||
Heat Deflection temperature | ºC | > 70 | ISO527-2 |
mechanical properties | |||
Elongation at break | % | > 4 | ISO527-2 |
Flexural strength | MPa | > 120 | ISO178 |
barcol hardness | > 40 | ASTM D2583 | |
Tensile strength | MPa | > 60 | ISO527-2 |
chemical properties | |||
Gel time | Second | 800 ± 60 | 25 ° C |
Acidity number | mg KOH / g | 30 ± 2 | |
Water absorption | % | Approximately 0.5 | ISO62- Test Method 3 |
Time gel test with 0.05% cobalt 10% and 105% MP50 peroxide
Maintenance
– In its packaging, store at a temperature of 5 to 25 degrees Celsius, in a dry environment away from direct sunlight. Avoid storing it near metal dryers and peroxides.
Resins for SMC-BMC plate and mass molding mixtures
These resins are designed to make BMC and SMC blends. These resins are used in the manufacture of auto parts, electrical parts, roofs, electrical circuit boxes, tanks and.. Among the characteristics of these resins are excellent mechanical properties, smooth and uniform surface with high gloss, high maturation strength.
Medium activity isophthalic polyester resin | Paya pol 440 |
High activity isophthalic polyester resin | Paya pol 450 |
Orthophthalic polyester resin | Paya pol 400 |
Chemical nature
Based on orthophthalic acid and standard glycols
Advantages
– Medium reactivity – Good lamination and wetting ability – Good mechanical properties including strain in failure and optimal HDI
applications
– Making pipes – Vessel – Fittings
Technical data
Appearance properties | |||
Color | Gardner | <2 |
Physical properties | |||
Solid Content | % | 64 ± 2 | |
Density | g / ml | 1.12 – 1.15 | |
Viscosity | cP | 400 ± 25 | 25 ° C |
Shrinkage | % | Approximately 2 | Internal Method, Linear Shrinkage |
Thermal properties | |||
Heat Deflection temperature | ºC | > 70 | ISO527-2 |
mechanical properties | |||
Elongation at break | % | > 4 | ISO527-2 |
Flexural strength | MPa | > 120 | ISO178 |
barcol hardness | > 40 | ASTM D2583 | |
Tensile strength | MPa | > 65 | ISO527-2 |
chemical properties | |||
Gel time | Second | 800 ± 60 | 25 ° C |
Acidity number | mg KOH / g | 35 ± 2 | |
Water absorption | % | Approximately 0.3 | ISO62- Test Method 3 |
Time gel test with 0.05% cobalt 10% and 105% MP50 peroxide
Maintenance
– In its packaging, store at a temperature of 5 to 25 degrees Celsius, in a dry environment away from direct sunlight. Avoid storing it near metal dryers and peroxides.
Polyester resin for pultrusion Pultrusion Polyester Resins
These resins are specially designed for the production of palletrogenic components, and among their properties are high HDT , excellent mechanical properties can be mentioned.
Isophthalic polyester resin | Paya pol 850 |
Orthophthalic polyester resin | Paya pol 840 |
RTM Resins for transfer molding
These resins are designed for resin injection ( RTM ) only.
Among the properties of the handle are suitable viscosity, low release of styrene, low shrinkage and fabrication of thin parts.
DCPD based resin suitable for auto parts | Paya pol 750 |
General purpose orthophthalic based resin | Paya pol 730 |
Isophthalic based resin | Paya pol 740 |
Wood Lacquer & Electric Insulators
Special wood resins are designed to cover wooden surfaces. The uniformity and smoothness of the surface, high gloss, excellent adhesion and resistance to various conditions are the properties of these resins, which are offered in both standing and polished skin.
Polishing resin containing paraffin | Paya pol 200 |
Glossy standing paraffin-free resin | Paya pol 220 |
Chemical nature – Based on isophthalic acid and standard glycols Advantages – Low reactivity – Good lamination and wetting ability – Good corrosion resistance – Flexibility – Crack resistance – Impact resistance – Low water absorption – Outstanding resistance To hydrolysis applications – Pipe construction – Vessel – Technical data connections
Appearance properties | |||
Color | Gardner | <2 |
Physical properties | |||
Solid Content | % | 63 ± 1 | |
Density | g / ml | 1.14 – 1.16 | |
Viscosity | cP | 400 ± 25 | 25 ° C |
Shrinkage | % | Approximately 1.8 | Internal Method, Linear Shrinkage |
Thermal properties | |||
Heat Deflection temperature | ºC | > 80 | ISO527-2 |
mechanical properties | |||
Elongation at break | % | > 4 | ISO527-2 |
Flexural strength | MPa | > 120 | ISO178 |
barcol hardness | > 40 | ASTM D2583 | |
Tensile strength | MPa | > 75 | ISO527-2 |
chemical properties | |||
Gel time | Second | 800 ± 60 | 25 ° C |
Acidity number | mg KOH / g | 22 ± 2 | |
Water absorption | % | Approximately 0.3 | ISO62- Test Method 3 |
Time gel test with 0.05% cobalt 10% and 105% MP50 peroxide Storage conditions – Store in packages at 5 to 25 ° C, in a dry place away from direct sunlight. Avoid storing it near metal dryers and peroxides.
Marine & Auto Resins for floating resins and car parts
Suitable viscosity, excellent fiber wetting, smooth and uniform surface, high mechanical properties and no resin leakage in vertical surfaces are the properties of this type of resin.
These resins can also be used in the manufacture of parts by vacuum bagging .
Isophthalic polyester resin for floats, boats, auto parts | Paya pol 420-B |
Orthophthalic polyester resin for floating, boat | Paya pol 525 Paya pol 575 Paya pol 545 Paya pol 800 |
Orthophthalic polyester resin for car parts | Paya pol 800 Paya pol 525 Paya pol 500 Paya pol 545 |
Special for stone mastic
Resins for stone industry Due to the extensive laboratory facilities and high technical capacity, the company is able to design special types of resins for different applications at the request of the customer. These include vinyl ester resins for chemical use.
Amine resin for mastic | Paya pol 2000 |
Ordinary resin for mastic | Paya pol 575-M Paya pol 500-M |
Resin for food | Paya pol 545-M Paya pol 525-M |
Special resin behind the stone | Paya pol 1500 |
UV drying resin | Paya pol 2500 |
Special for stone glue
Pitches for the construction of putty, glue Stone Putty & Stone Adhesive Resins
These resins Bnvtvnh types of polyester and adhesive stone is designed for cars. Their properties include good dryness, high mechanical properties, good filler and ideal adhesion.
Resin for stone mastic | Paya pol 2000 |
Resin for stone putty | Paya pol 3000 |
Resin for stone adhesive | Paya pol 4000 |
Special stone putty
Solid Surface Resins for artificial stone
These resins are used to make monolithic stones and various types of artificial granite. Among their properties are high HDT level uniformity , scratch resistance and polishing.
Orthophthalic based resin for artificial stone with general application | Paya pol 610 |
ISO-NPG based resin modified with methacrylate | Paya pol 630 |
ISO based resin for granite and cabinets | Paya pol 650 |